تعجيل خصائص المحفز الضوئي بأكسيد السيلينيوم متناهي الصغر بترسيب البلاتينيوم
Enhancement of photocatalytic properties of Ga2O3-SiO2 nanoparticles by Pt deposition
 
الموضوع : علوم البيئة 
لغة الوثيقة : الانجليزية 
المستخلص : Ga2O3-SiO2 nanoparticles were prepared by a sol-gel method and Pt was then immobilized on their surface via photo-assisted deposition (PAD). The produced samples were characterized using X-ray diffraction (XRD), ultraviolet and visible spectroscopy, photoluminescence emission spectroscopy, and surface area measurements. The catalytic performances of the Ga2O3-SiO2 and Pt/ Ga2O3-SiO2 samples were evaluated for the degradation of cyanide using visible light. XRD and EDX results showed that the Pt was well dispersed within the Ga2O3-SiO2 phase and was detected on the surface of the catalyst, which confirmed the successful loading of Pt ions by the PAD method. BET results revealed that the surface area of Ga2O3-SiO2 was higher than that of Pt/Ga2O3-SiO2. 0.3 wt% Pt/Ga2O3-SiO2 exhibited the highest photocatalytic activity for degradation of cyanide under visible light. The catalyst could be reused with no loss in activity for the first 10 cycles. 
ردمد : 0253-9837 
اسم الدورية : SCIENCE PRESS, 16 DONGHUANGCHENGGEN NORTH ST, BEIJING 100717, PEOPLES R CHINA 
المجلد : 34 
العدد : 1 
سنة النشر : 1434 هـ
2013 م 
نوع المقالة : مقالة علمية 
تاريخ الاضافة على الموقع : Monday, June 3, 2013 

الباحثون

اسم الباحث (عربي)اسم الباحث (انجليزي)نوع الباحثالمرتبة العلميةالبريد الالكتروني
E. S. BAEISSABAEISSA, E. S. باحث  
R. M. MOHAMEDMOHAMED, R. M. باحث redama123@yahoo.com

الملفات

اسم الملفالنوعالوصف
 35612.pdf pdfEnhancement of photocatalytic properties of Ga2O3-SiO2 nanoparticles by Pt deposition

الرجوع إلى صفحة الأبحاث